ACTFLEX 929 HV
high-build, single-component polyurethan
High viscosity, moisture-cured polyurethane waterproofing membrane for internal and external wet areas, roofs, planter boxes, and retaining walls.
ACTFLEX 929 HV is a Class III, high-build, single-component polyurethane waterproofing membrane designed for use in under-tile, non-exposed, and protected external applications. It cures by atmospheric moisture to form a tough, flexible, and elastomeric film resistant to immersion, chemicals, and root intrusion.
Compliant with AS3740:2021 (Waterproofing of Wet Areas within Domestic Buildings) and AS4654.2:2012 (Waterproofing Membranes for External Above-Ground Use), ACTFLEX 929 HV ensures reliability across demanding waterproofing environments such as terraces, roofs, planters, retaining walls, sub-stations, bridges, and parking decks
specs
Technical Specifications.
Waterproof Time:
48 hours at 25°C, 50% RH (after final coat).
Coverage:
8–10 m² per 20 kg set at 1.2 mm total DFT (depending on substrate porosity).
Usable period after opening:
Touch dry time minimum:
Tack free: 6 hrs @ 25°C
Recoat: 4–6 hrs
Full cure: 48 hrs @ 25°C (1.2 mm DFT)
Vapor Pressure @ 25oC:
Pass (ASTM E96 Moisture Vapour Transmission).
Application Temperature:
10°C-26°C
Shelf Life:
12 months in unopened containers
Membrane
Classification:
Class III
Colour:
Grey
Tack Free Time:
6 hours @ 25°C, 50% RH.
Recoat Time:
4–6 hours; max 48 hours between coats.
Elongation at Break:
>600%
Recommended
Thickness:
Wall applications: 1.0 mm
Floors/upturns: 1.2 mm
Planter boxes/retaining walls: 1.5 mm
Chemical
Resistant:
Excellent resistance to mild chemicals, corrosion, and root intrusion.
Full Cure:
48 hours at 25°C (1.2 mm total DFT).
Chemical Base:
Single-component moisture-cured polyurethane.
Cure Mechanism:
Chemical reaction with atmospheric moisture.
Tear Propagation
Resistance:
High; non-sag thixotropic consistency.
Service
Temperature:
–10°C to +60°C (continuous service).
Solid Contents:
90% ± 2%.
Bond Strength:
Density:
1.1–1.3 g/cm³.
Compressive
Strength:
Flow:
Acceptance of Cyclic Movement:
Thixotropic (non-slump).
Dimensional Stability:
Thixotropic (non-slump).
Control Elongation at Break:
Thixotropic (non-slump).
Control Tensile Strength:
Thixotropic (non-slump).
Water Immersion Elongation at Break:
Thixotropic (non-slump).
Water Immersion Tensile Strength:
Thixotropic (non-slump).
Detergent Immersion Elongation at Break:
Thixotropic (non-slump).
Detergent Immersion Tensile Strength:
Thixotropic (non-slump).
Heat Aging Elongation at Break:
Thixotropic (non-slump).
Heat Aging Tensile Strength:
Thixotropic (non-slump).
Field Seam Strength:
Thixotropic (non-slump).
Temperature Resistance:
Water Vapour Transmission
Thixotropic (non-slump).
Water Vapour Transmission:
Thixotropic (non-slump).
Application Method:
Thixotropic (non-slump).
VOC Content:
Thixotropic (non-slump).
Mixing Ratio:
Thixotropic (non-slump).
Viscosity:
Thixotropic (non-slump).
Storage Temperature:
Thixotropic (non-slump).
Flash Point:
Thixotropic (non-slump).
UV Resistance:
Thixotropic (non-slump).
Hydrostatic Pressure Resistance:
Thixotropic (non-slump).
Water Vapour Transmission Rate (WVTR):
Thixotropic (non-slump).
Abrasion Resistance:
Thixotropic (non-slump).
Bacterial/Algae Resistance:
Thixotropic (non-slump).
Application Time:
Thixotropic (non-slump).
Environmental Impact:
Thixotropic (non-slump).
Packaging Sizes:
Thixotropic (non-slump).
Hardness:
Thixotropic (non-slump).
Adhesion to Substrate:
Thixotropic (non-slump).
Appearance After Curing:
Thixotropic (non-slump).
Clean-up Requirements:
Thixotropic (non-slump).
Certification Standards:
Thixotropic (non-slump).