ACTFLEX 988 CWP
two-part flexible cementitious acrylic waterproofing membrane
High-performance, two-part flexible cementitious acrylic waterproofing membrane for positive and negative hydrostatic pressure applications.
ACTFLEX 988 CWP is a two-part flexible cementitious acrylic waterproofing membrane formulated for use in both internal and external wet areas, including below-ground waterproofing, tanks, retaining walls, and swimming pools. The product combines a polymer liquid (Part A) with a reactive powder (Part B) to form a dense, flexible coating resistant to water pressure and efflorescence migration.
Compliant with AS4858-2004 and AS4654.1:2012, ACTFLEX 988 CWP delivers hydrostatic pressure resistance up to 350 kPa (3.5 bar) and elongation of 217%, ensuring durability in submerged and high-pressure environments. It is non-toxic, non-flammable, low VOC, and suitable for both positive and negative side waterproofing.
specs
Technical Specifications.
Waterproof Time:
48 hours @ 25°C, 50% RH (for non-submerged applications).
Coverage:
20 kg kit covers approximately 8–10 m² @ 1.2 mm DFT (two coats).
Usable period after opening:
Approx. 2 hours pot life @ 23°C, 50% RH.
Touch dry time minimum:
Recoat: 4–6 hours @ 25°C
Tack Free: 6 hours
Full Cure: 48 hours @ 25°C (1.2 mm DFT)
Confined underground areas: 7 days
Constant water exposure: 10+ days
Vapor Pressure @ 25oC:
Not a vapor barrier; suitable for hydrostatic pressure resistance only.
Application Temperature:
10°C-26°C
Shelf Life:
12 months (unopened, stored between 10–22°C, 50% RH).
Membrane
Classification:
Class II (AS4654.1 / AS4858)
Colour:
Khaki Green
Tack Free Time:
6 hours @ 25°C, 50% RH
Recoat Time:
4–6 hours @ 25°C, 50% RH
Elongation at Break:
217% ± 5%
Recommended
Thickness:
1.2 mm (Wet Areas, PVC Panels)
1.5 mm (Underground or Submersion)
Chemical
Resistant:
Excellent resistance to efflorescence, mild acids, and alkalis.
Full Cure:
48 hours (1.2 mm DFT)
7–10 days for water immersion.
Chemical Base:
Cementitious polymer composite
Cure Mechanism:
Hydraulic cementitious reaction and acrylic coalescence
Tear Propagation
Resistance:
High (Shore A 50A)
Service
Temperature:
Solid Contents:
65% ± 2%
Bond Strength:
Density:
~1.65 g/cm³ mixed
Compressive
Strength:
10 MPa (typical cementitious performance)
Flow:
10 MPa (typical cementitious performance)
Acceptance of Cyclic Movement:
Dimensional Stability:
Control Elongation at Break:
Control Tensile Strength:
Water Immersion Elongation at Break:
Water Immersion Tensile Strength:
Detergent Immersion Elongation at Break:
Detergent Immersion Tensile Strength:
Heat Aging Elongation at Break:
Heat Aging Tensile Strength:
Field Seam Strength:
Temperature Resistance:
Water Vapour Transmission
Water Vapour Transmission:
Application Method:
VOC Content:
Mixing Ratio:
Viscosity:
Storage Temperature:
Flash Point:
UV Resistance:
Hydrostatic Pressure Resistance:
Water Vapour Transmission Rate (WVTR):
Abrasion Resistance:
Bacterial/Algae Resistance:
Application Time:
Environmental Impact:
Packaging Sizes:
Hardness:
Adhesion to Substrate:
Appearance After Curing:
Clean-up Requirements:
Certification Standards:
calculator
Coverage Calculator.
Based on a manufacturers average recommended coverage of 20 kg kit covers approximately 8–10 m² @ 1.2 mm DFT (two coats).
Required:
250 Lr
3d
Application Model