ACTFLEX CRACK PRO 1200PS
crack injection, structural bonding, anchoring
Two-component structural epoxy adhesive
CRACK PRO 1200PS is a high-strength, medium-modulus, two-component epoxy adhesive for structural crack repair by pressure injection and gravity feed, bonding freshly mixed concrete to hardened concrete, and filling voids in concrete and masonry. It seals and structurally reconnects cracks from 3 mm to 8 mm wide and cures to a thin impermeable layer.
It is also used for port injection repair of vertical cracks, anchoring bolts and dowels, epoxy mortar and spall repair with kiln-dried aggregate, and high-friction surface treatments on concrete and asphalt.
specs
Technical Specifications.
Waterproof Time:
After full cure
Coverage:
Crack and void dependent
Usable period after opening:
Approx. 1 hour after application (spall repair)
Touch dry time minimum:
Tack free: 3–5 hours @ 23°C
Full cure: 24 hours
Vapor Pressure @ 25oC:
Impermeable cured epoxy layer
Application Temperature:
5°C – 35°C substrate and ambient
Shelf Life:
24 months
Membrane
Classification:
Structural Epoxy Injection Resin
Colour:
Clear to light amber
Tack Free Time:
3–5 hours @ 23°C
Recoat Time:
After tack free
Elongation at Break:
Medium modulus system
Recommended
Thickness:
Injection dependent
Minimum adhesive depth: 12mm
Chemical
Resistant:
Yes – resistant to industrial chemicals
Full Cure:
24 Hours
Chemical Base:
Two-component structural epoxy
Cure Mechanism:
Chemical reaction (1:1 mix ratio)
Tear Propagation
Resistance:
High structural bonding performance
Service
Temperature:
−7°C to +50°C after curing
Solid Contents:
100% reactive epoxy system
Bond Strength:
Density:
Compressive
Strength:
55.22 MPa (ASTM D695-15)
Flow:
55.22 MPa (ASTM D695-15)
Acceptance of Cyclic Movement:
Viscosity: 2,210 cps at 25°C
Dimensional Stability:
Viscosity: 2,210 cps at 25°C
Control Elongation at Break:
Viscosity: 2,210 cps at 25°C
Control Tensile Strength:
Viscosity: 2,210 cps at 25°C
Water Immersion Elongation at Break:
Viscosity: 2,210 cps at 25°C
Water Immersion Tensile Strength:
Viscosity: 2,210 cps at 25°C
Detergent Immersion Elongation at Break:
Viscosity: 2,210 cps at 25°C
Detergent Immersion Tensile Strength:
Viscosity: 2,210 cps at 25°C
Heat Aging Elongation at Break:
Viscosity: 2,210 cps at 25°C
Heat Aging Tensile Strength:
Viscosity: 2,210 cps at 25°C
Field Seam Strength:
Viscosity: 2,210 cps at 25°C
Temperature Resistance:
Water Vapour Transmission
Viscosity: 2,210 cps at 25°C
Water Vapour Transmission:
Viscosity: 2,210 cps at 25°C
Application Method:
Viscosity: 2,210 cps at 25°C
VOC Content:
Viscosity: 2,210 cps at 25°C
Mixing Ratio:
Viscosity: 2,210 cps at 25°C
Viscosity:
Viscosity: 2,210 cps at 25°C
Storage Temperature:
Viscosity: 2,210 cps at 25°C
Flash Point:
Viscosity: 2,210 cps at 25°C
UV Resistance:
Viscosity: 2,210 cps at 25°C
Hydrostatic Pressure Resistance:
Viscosity: 2,210 cps at 25°C
Water Vapour Transmission Rate (WVTR):
Viscosity: 2,210 cps at 25°C
Abrasion Resistance:
Viscosity: 2,210 cps at 25°C
Bacterial/Algae Resistance:
Viscosity: 2,210 cps at 25°C
Application Time:
Viscosity: 2,210 cps at 25°C
Environmental Impact:
Viscosity: 2,210 cps at 25°C
Packaging Sizes:
Viscosity: 2,210 cps at 25°C
Hardness:
Viscosity: 2,210 cps at 25°C
Adhesion to Substrate:
Viscosity: 2,210 cps at 25°C
Appearance After Curing:
Viscosity: 2,210 cps at 25°C
Clean-up Requirements:
Viscosity: 2,210 cps at 25°C
Certification Standards:
Viscosity: 2,210 cps at 25°C
calculator
Coverage Calculator.
Based on a manufacturers average recommended coverage of Crack and void dependent
Required:
NaN Lr
pdfs
Product Documentation.
Compliance Testing Report 1 (PDF Download)
Compliance Testing Report 2 (PDF Download)
Compliance Testing Report 3 (PDF Download)
Low VOC Certificate (PDF Download)
Product How To Guide (PDF Download)
3d
Application Model