ACTFLEX Crystal Coat
Industrial & Decorative Flooring
Two-Component High Build Epoxy Floor Coating
ACTFLEX CRYSTAL COAT is a high-build, 100% solids, two-component (2:1) cycloaliphatic epoxy system designed for heavy-duty commercial and industrial floors. Its low-viscosity, solvent-free formulation ensures superior chemical resistance, minimal color change, and long-term durability. It can also be used as an epoxy screed system for thicknesses 1–90mm, achieving up to 60 MPa compressive strength—ideal for high-traffic and sloped areas requiring maximum structural performance.
specs
Technical Specifications.
Waterproof Time:
After full cure (7 days)
Coverage:
0.3mm → 3.3m²/L
0.6mm → 1.7m²/L
1.0mm → 1.1m²/L
Usable period after opening:
Light Traffic: 24 hours
Full Heavy Traffic & Chemical Resistance: 7 days
Touch dry time minimum:
48 Hours at 25°C & 50% RH
Vapor Pressure @ 25oC:
Moisture-sensitive during curing
Application Temperature:
10°C - 30°C
Shelf Life:
9 months
Membrane
Classification:
Two-Component Epoxy Floor Coating
Colour:
Clear or Coloured
Tack Free Time:
6–8 hour
Recoat Time:
6–24 hours
Elongation at Break:
<100%
Recommended
Thickness:
0.2mm – 1.0mm application range
Chemical
Resistant:
Yes – industrial grade
Full Cure:
48 Hours at 25°C & 50% RH
Chemical Base:
Cycloaliphatic Epoxy (100% Solids)
Cure Mechanism:
Chemical reaction – 2:1 mix ratio
Tear Propagation
Resistance:
High abrasion resistant
Service
Temperature:
Industrial flooring environments
Solid Contents:
100%
Bond Strength:
Excellent adhesion to primed substrates
Density:
Compressive
Strength:
High mechanical performance (industrial floor grade)
Shore A: 95
Shore D: 60
Flow:
High mechanical performance (industrial floor grade)
Shore A: 95
Shore D: 60
Acceptance of Cyclic Movement:
Dimensional Stability:
Control Elongation at Break:
Control Tensile Strength:
Water Immersion Elongation at Break:
Water Immersion Tensile Strength:
Detergent Immersion Elongation at Break:
Detergent Immersion Tensile Strength:
Heat Aging Elongation at Break:
Heat Aging Tensile Strength:
Field Seam Strength:
Temperature Resistance:
Water Vapour Transmission
Water Vapour Transmission:
Application Method:
VOC Content:
Mixing Ratio:
Viscosity:
Storage Temperature:
Flash Point:
UV Resistance:
Hydrostatic Pressure Resistance:
Water Vapour Transmission Rate (WVTR):
Abrasion Resistance:
Bacterial/Algae Resistance:
Application Time:
Environmental Impact:
Packaging Sizes:
Hardness:
Adhesion to Substrate:
Appearance After Curing:
Clean-up Requirements:
Certification Standards:
calculator
Coverage Calculator.
Based on a manufacturers average recommended coverage of 0.3mm → 3.3m²/L
0.6mm → 1.7m²/L
1.0mm → 1.1m²/L