FORCRETE 100
high-build, high-strength repair mortar ideal for structural patching
FORCRETE 100 is a high-build, high-strength repair mortar ideal for structural patching in vertical, horizontal, and overhead concrete repairs. Designed for critical infrastructure applications, FORCRETE 100 offers ≥70 MPa compressive strength, shrinkage compensation, and excellent adhesion to concrete and steel. FORCRETE 100 is polymer-modified, fibre-reinforced, and resists chloride ingress, carbonation, and abrasion for long-term durability in marine and exposed environments.
specs
Technical Specifications.
Waterproof Time:
Coverage:
2.1 g/cm³, 11.1–11.5 L yield approx. based on 3.6L water and 20 kg mix
Usable period after opening:
No walk-on time listed – protect from traffic and rain during first 24 hr
Touch dry time minimum:
Initial set ~1.5 hrs
Final set ~2.5 hr
Vapor Pressure @ 25oC:
Shrinkage-related microstrain only, not WVTR; product is not vapor-permeable (repair mortar)
Application Temperature:
5°C – 35°C
Shelf Life:
12 months (dry, unopened)
Membrane
Classification:
Colour:
Grey
Tack Free Time:
Recoat Time:
Next layer (for over 100 mm vertical or 180 mm horizontal) applied when first layer is stiff but not fully cure
Elongation at Break:
Recommended
Thickness:
Horizontal: 10–180 mm
Vertical/Overhead: 5–100 mm
Chemical
Resistant:
Resistant to carbonation and chloride ingress; not a full chemical barrie
Full Cure:
28 Days (70 MPa)
Chemical Base:
Cement-based, polymer-modified with fibres
Cure Mechanism:
Hydraulic cement reaction + polymer binding
Tear Propagation
Resistance:
Service
Temperature:
Solid Contents:
Bond Strength:
>2 MPa to concrete
Density:
2.1 g/cm³ (wet)
Compressive
Strength:
25 MPa @ 1 day
51 MPa @ 7 days
70 MPa @ 28 days
Flow:
25 MPa @ 1 day
51 MPa @ 7 days
70 MPa @ 28 days
Acceptance of Cyclic Movement:
Dimensional Stability:
Control Elongation at Break:
Control Tensile Strength:
Water Immersion Elongation at Break:
Water Immersion Tensile Strength:
Detergent Immersion Elongation at Break:
Detergent Immersion Tensile Strength:
Heat Aging Elongation at Break:
Heat Aging Tensile Strength:
Field Seam Strength:
Temperature Resistance:
Water Vapour Transmission
Water Vapour Transmission:
Application Method:
VOC Content:
Mixing Ratio:
Viscosity:
Storage Temperature:
Flash Point:
UV Resistance:
Hydrostatic Pressure Resistance:
Water Vapour Transmission Rate (WVTR):
Abrasion Resistance:
Bacterial/Algae Resistance:
Application Time:
Environmental Impact:
Packaging Sizes:
Hardness:
Adhesion to Substrate:
Appearance After Curing:
Clean-up Requirements:
Certification Standards:
calculator
Coverage Calculator.
Based on a manufacturers average recommended coverage of 2.1 g/cm³, 11.1–11.5 L yield approx. based on 3.6L water and 20 kg mix